Chemical Properties
White powder.Soluble in acids and ammonium hydroxide; insoluble in water.
Uses
Dental cements; phosphors; conversion coating
of steel, aluminum, and other metal surfaces.
Uses
Zinc phosphate (ZP), barium metaborate, and strontium chromate pigments are also common ingredients in corrosion-inhibiting coatings. Thin wash-inhibiting primers are often formulated with chromate or phosphate pigments that are introduced in a synthetic polymeric binder such as a vinyl chloride copolymer. The variety of inorganic corrosion-inhibiting pigments includes also lead carbonate, strontium chromate, zinc oxide, and ZP.
Zinc phosphate (ZP) is the most commercially successful non-toxic inhibitive pigment used in paint formulations. Furthermore, the use of phosphates does not represent an excessive cost, and their application is even easier than other proposed alternatives for chromate pigments. This is the anticorrosive pigment most frequently used in paints. The massive use of nontoxic and environmentally acceptable ZPs developed an immense pressure for regulations that prohibited the use of red lead and chromated anticorrosion pigments. Experimental results suggest that ZP and all phosphate-based pigments (zinc-aluminum polyphosphate, ZP modified with organic corrosion inhibitor, etc.) exhibit improved anticorrosion efficiency when their concentration is increased.
reaction suitability
reagent type: catalyst
core: zinc
Safety Profile
Moderately toxic by
intraperitoneal route. When heated to
decomposition it emits acrid smoke and
irritating fumes.
Synthesis
Zinc phosphate is insoluble in water or ethanol, soluble in dilute acid, ammonia and ammonium salt solution. Zinc phosphate can be obtained by reacting phosphoric acid solution and zinc oxide, or by reacting trisodium phosphate and zinc sulfate.
Properties and Applications
|
TEST ITEMS
|
SPECIFICATION
|
|
APPEARANCE
|
White Powder
|
|
ZINC CONTENT
|
45% min
|
|
HEAT RESISTANCE
|
600 °C min
|
|
DENSITY
|
4.00 g/cm
3
|
|
LIGHT FASTNESS
|
7~8
|
|
ACID RESISTANCE
|
4
|
|
ALKALI RESISTANCE
|
4
|
|
FASTNESS TO BLEEDING
|
5
|
|
OIL ABSORPTION
|
25-35 g/100g
|
|
pH VALUE
|
6-8
|
|
MOISTURE
|
1.5%max
|
|
RESIDUE ON SIEVE (45um) %
|
0.5% max
|
|
VOLATITE 105 °C
|
1.0% max
|
|
TINTING STRENGTH
|
100-105 %
|