1307-96-6

Raw materials And Preparation Products

Hazard Information

Description

This is obtained as an olive-green powder by heating the metal in air or steam or by thermal decomposition of the hydroxide, carbonate or nitrate. It has the sodium chloride lattice and is antiferromagnetic below 292°K. When heated in oxygen above 400° the black oxide Co3O4 is obtained. This oxide is isomorphous with magnetite Fe3O4, and has tetrahedrally surrounded cobalt(II) ions and octahedrally surrounded cobalt(III) ions. Both these oxides are readily reduced to the metal by heating in hydrogen or with carbon. The reactions of CoO with silica, alumina and zinc oxide are used to form pigments in the ceramic industry.

Chemical Properties

Cobalt oxide is a high-valent oxide of cobalt, with a theoretical cobalt content of 71.06% and an oxygen content of 28.94%, which is a black amorphous powder. Cobalt oxide is a kind of unstable and impossible free state compound, usually refers to the cobalt oxide are attached with a certain amount of cobalt tetraoxide when heated cobalt oxide is reduced to cobalt tetraoxide. The theoretical cobalt content of cobalt tetraoxide is 73.43% and the oxygen content is 26.57%, with the appearance of gray-black or black powder.

The cobalt oxide used in batteries is cobalt tetraoxide, which has a spinel structure. It can be used as anode material for lithium-ion batteries and is also the main raw material for the preparation of lithium cobaltate, the cathode material for lithium-ion batteries.

Physical properties

The commercial product is usually dark grey powder, but the color may vary from olive geeen to brown depending on particle size; density 6.44 g/cm³, which also may vary between 5.7 to 6.7 g/cm³, depending on the method of preparation; melts around 1,830°C; insoluble in water; soluble in acids and alkalis.

Flammability and Explosibility

Notclassified(100%)

Structure and conformation

Green cobalt(II) oxide (CoO) has the rock salt (NaCl) structure. It is easily oxidized with water and oxygen to brown cobalt(III) hydroxide (Co(OH)3). At temperatures of 600℃-700℃, CoO oxidizes to the blue cobalt (II,III) oxide (Co3O4), which has a spinel structure. Black cobalt(III) oxide (Co2O3) also exists. Cobalt oxides are antiferromagnetic at low temperature: CoO (Ne′el temperature 18℃/291K) and Co3O4 (Ne′el temperature: 2233℃/40K), which is analogous to magnetite (Fe3O4), with a mixture of 12 and 13 oxidation states.

Material Safety Data Sheet(MSDS)

Questions And Answer

• Cobalt oxides

  Cobalt oxides have three oxidation states, namely: (i) cobaltous oxide (cobalt monoxide or cobalt [II] oxide) with CoO chemical formula, (ii) cobaltic oxide (cobalt [III] oxide) with Co2O3 chemical formula and (iii) cobaltosic oxide (cobalt [II, III] oxide) with Co3O4 chemical formula, which is an antiferromagnetic material. The first and the last oxidation states have a cubic crystal structure.
  Cobalt oxide is used in pigments for ceramics, in glass coloring and decolorization, as oxidation catalyst for drying oils, and fast-drying paints and varnishes, in preparation of cobalt-metal catalysts, and cobalt powder for binder in sintered tungsten carbide; in semiconductors.;

• Uses

  Cobalt(II) oxide is used as a pigment for ceramics and paints; for drying paints, varnishes and oils; for coloring glass; as a catalyst; and for preparation of other cobalt salts. The commercial product is a mixture of cobalt oxides. ;

• Preparation

  Cobalt(II) oxide is prepared by heating cobalt(II) carbonate, CoCO3, cobalt(III) oxide, Co2O3 or tricobalt tetroxide, Co3O4, at high temperatures in a neutral or slightly reducing atmosphere:
  CoCO3 → CoO + CO2 ;

• Toxicity

  Cobalt(II) oxide is moderately toxic by ingestion and subcutaneous and intratracheal routes.
  LD50 oral (rat): 202 mg/kg ;

Spectrum Detail

Well-known Reagent Company Product Information

Supplier

Related Products