4-PHENYLETHYNYLPHTHALIC ANHYDRIDE 화학적 특성, 용도, 생산

• 개요

  4-Phenylethynylphthalic anhydride (PEPA) is a phthalic anhydride derivative with a phenylethynyl substituent in the 4-position.PEPA is commonly used as a reactive capping agent for polyimide synthesis and aromatic oligo-polyimides. Fluorinated aromatic oligoimides terminated with a phenylethynyl substituent melt completely in the range of 250-350 °C to form a low viscosity liquid. The melt viscosity of oligoimides increases with increasing molecular weight. After thermal curing at 371 °C, the thermoset polyimide resins produced show good thermal and mechanical properties. They showed a high glass transition temperature (Tg) of 300 °C, a flexural strength of 135.5 MPa, a flexural modulus of 3.1 GPa, a tensile strength of 65.7 MPa, and an elongation at break of 3.9%.

• 화학적 성질

  Light yellow to light yellow-green crystal or powder

• 제조 방법

  The preparation of 4-phenylethynylphthalic anhydride is as follows:4-phenyl ethynyl dimethyl phthalate (33.6 g) was suspended in a mixed medium comprising water and methanol and a 25% by mass aqueous solution of sodium hydroxide (40 g) was dropwise added thereto with stirring. The resultant reaction mixture was stirred at 60° C. for 3 hours and, then, after confirming the completion of the reaction, cooled to the inside temperature of 30° C. Thereafter, 1 g of active carbon was added thereto, and, then, stirred for 30 minutes maintaining the same temperature. The resultant mixture was filtered to remove the active carbon, and rinsed with water. The filtrate and a rinsing solution were combined and, then, toluene and ethyl acetate were added to the resultant mixture. Concentrated hydrochloric acid (28 g) was dropwise added to the resultant 2-layered reaction mixture. The mixture was stirred for 30 minutes at room temperature and was allowed to stand, so that an organic layer containing 4-phenyl ethynyl phthalic acid was separated. After partially concentrating the organic layer, acetic anhydride (17 g) was added thereto, and the reaction mixture was refluxed with heating for 4 hours. After the reaction was completed, the resultant reaction mixture was cooled, so that 4-phenyl ethynyl phthalic anhydride was precipitated as a crystal. The crystal was filtered, rinsed and dried, to thereby obtain 26.6 g of 4-phenyl ethynyl phthalic anhydride as a pale yellow crystal. The yield was 94% on the basis of 4-phenyl ethynyl dimethyl phthalate.

  

4-PHENYLETHYNYLPHTHALIC ANHYDRIDE 준비 용품 및 원자재

4-PHENYLETHYNYLPHTHALIC ANHYDRIDE 공급 업체

Global(196)Suppliers

4-PHENYLETHYNYLPHTHALIC ANHYDRIDE 관련 검색