Grade | YH-791 SBS1301 | YH-791H SBS1301-1 | YH-792 SBS1401 | YH-796 SBS1201 | YH-805 SBS4452 | YH-815 SBS4412 | SBS4303-2 |
S/B Content % | 30/70 | 30/70 | 40/60 | 20/80 | 40/60 | 40/60 | 40/60 |
Volatile (≤%) | 0.7 | 0.7 | 0.7 | 0.7 | 0.7 | 0.20 | 0.7 |
300% fixed elongation stress (≥MPa) | 15.0 | 2.2 | 3.5 | 1.4 | 2.5 | 2.5 | 2.2 |
Tensile Strength (≥MPa) | 2.0 | 16.0 | 24.0 | 8.0 | 14.0 | 17.0 | 8.0 |
Elongation at break (≥%) | 40 | 700 | 730 | 700 | 900 | 700 | 550 |
Permanent deformation (≤%) | 700 | 40 | 55 | 30 | 50 | 55 | 40 |
Shore hardness (A) | ≥68 | ≥68 | ≥85 | ≥58 | ≥52 | ≥83 | ≥70 |
The melt flow rate | 0.10~5.00 | 0.50~2.50 | 0.1~5.00 | 0.10~5.00 | 0.01~0.10 | 0.01~0.50 | 0.00~1.00 |
structure | Linear | Linear | Linear | Linear | Radial | Radial | Radial |
Main application | Adhesive Asphalt modification | Asphalt modification | Adhesive Sealants Shoe material Asphalt modification Plastic modification | Adhesive Polymer modification | Shoe material | Shoe material | Asphalt modification |
Thermoplastic styrene butadiene rubber has many uses in adhesives, and can be used to produce contact adhesives instead of chloroprene - phenolic adhesives. Production of SBS grafting adhesive, or combined with neoprene rubber to produce CR-SBS mixed grafting adhesive; Manufacture ordinary shoe glue, shoe sole coating agent; Manufacture special adhesive for luggage; Production of solvent-based pressure sensitive agent, hot melt adhesive, hot melt pressure sensitive adhesive; Production of paper plastic film adhesive, polyolefin adhesive; Production of building glue, building sealant, CR-SBS sealant, waterproof coil special adhesive; Modified asphalt, etc.