Titandisilicid

Gefahreninformationscode (GHS)

• Bildanzeige (GHS)

  

• Gefahrenhinweise

  H228：Entzündbarer Feststoff.

  H315：Verursacht Hautreizungen.

  H319：Verursacht schwere Augenreizung.

  H335：Kann die Atemwege reizen.

• Sicherheit

  P210：Von Hitze, heißen Oberflächen, Funken, offenen Flammen und anderen Zündquellenarten fernhalten. Nicht rauchen.

  P261：Einatmen von Staub vermeiden.

  P280：Schutzhandschuhe/Schutzkleidung/Augenschutz tragen.

  P305+P351+P338：BEI KONTAKT MIT DEN AUGEN: Einige Minuten lang behutsam mit Wasser spülen. Eventuell vorhandene Kontaktlinsen nach Möglichkeit entfernen. Weiter spülen.

  P405：Unter Verschluss aufbewahren.

TITANIUM SILICIDE Chemische Eigenschaften,Einsatz,Produktion Methoden

• Chemische Eigenschaften

  orthorhombic black powder(s), a=0.8236 nm, b=0.4773nm, c=0.8523 nm; hardness 4.5 Mohs; resistivity 123μοhm· cm can be prepared by reaction of the elements; used in special alloy applications, as a flame-resistant coating material, also as 99.5 or 99.9% pure material, as a sputtering target in the fabrication of integrated circuits [HAW93] [STR93] [CER91]

• Verwenden

  In special alloy applications, as a flame or blast impingement-resistant coating material.

• Verwenden

  Titanium silicide is used in the semiconductor industry. It is also used in the fabrication of transistors.

• Synthese

  (1) PREPARATION FROM THE ELEMENTS
  Ti + 2 Si = TiSi2
  The silicides are prepared by fusing or sintering intimate stoichiometric mixtures of the elements (in powder form). The reaction is carried out in sintered clay or ceramic crucibles, placed in a Tammann furnace under a blanket of Ar. In all three cases the reaction takes place at a relatively low temperature and is highly exothermic; therefore, one should work with gram quantities only.
  (2) ALUMINOTHERMIC METHOD
  Ignition of a mixture of, for example, 200 g. of Al powder, 250 g. of S, 180 g. of SiOa and 15 g. of TiO2 (or 40 g. of K2TiF6 ), covered with a thin layer of Mg, yields an ingot containing, in addition to Si and Al, small, iron-gray tetragonal pyramids of TiSi2 .
  (3) ELECTROLYTIC PREPARATION
  The pure, crystalline silicides ar e obtained by melt electrolysis of a mixture of, for example, 10K2SiF6 + TiO2 at about 900°C, using an iron cathode; alternately, electrolysis of TiO2 dissolved in a melt of silicate may be used.
  