Sodium polyacrylate(90039-04-7) is the sodium salt of polyarylic acid. As a chemical polymer, it has various kinds of application in consumer products. It is capable of absorbing extremely high amount of water which can reach up to as much as 200 to 300 times its mass; therefore, it is used in agriculture industry and is infused in the soil of many plants to maintain the moisture of plant. It can be commonly used as a sequestering agent, or chelating agent in many detergents. It can also be used as a thickening agent to be used in diapers and hair gels because of its high capability of absorbing and holding water. Furthermore, it can be included in the coatings of sensitive electrical wiring to remove moisture in the wires.
Sodium polyacrylate(9003-04-7) is a commonly used dispersant, also known as 2-sodium acrylate homopolymer, S sodium polyacrylate. It is colorless or light yellow viscous liquid in room temperature, and non-toxic, alkaline, insoluble in organic solvents such as ethanol, acetone but easily soluble in water and aqueous sodium hydroxide. However, for aqueous solution of calcium hydroxide, magnesium hydroxide, due to the increase of alkaline metal ions, it is first dissolved and then precipitated. It can work without entrustment under alkaline conditions or being concentrated for several folds with molecular weight of about 500-3000. It can disperse the microcrystalline or sediment of calcium carbonate, calcium sulfate salts into the water without precipitation, and thus achieving the purpose of preventing entrustment. Besides used as the descaling dispersant in power plants, chemical plants, fertilizer plants, refineries and air conditioning systems, cooling water system, it is also widely used in industries like paper and textile, ceramics, paints, building materials. When used as a paper coating dispersant, it has a relative molecular mass in 2000-4000. When coating concentration is 65% to 70%, it can still have a good rheology and aging stability. The product in molecular weight from 1000 to 3000 is used as water quality stabilizer as well as scaling control agent of concentrated black liquor. Products with molecular weight higher than 100,000 is used as coatings thickener and water retention agent, which can increase the viscosity of synthetic emulsion such as carboxylated styrene-butadiene latex and acrylate emulsion latex and prevent the water from being separated out as well as maintain the stability of the coating system . Product of molecular weight of 1 million or more can be used as a flocculant. It can also be used as super absorbent polymer, soil conditioners, as well as a thickening agent and emulsion dispersant in the food industry.
The molecular structure of sodium polyacrylate molecule is water soluble linear polymers. Small molecular weight molecule is as liquid with large molecule counterparts shown as solid. Solid product is shown as a white powder or granules, and is odorless, water-swellable, and soluble in aqueous caustic soda. Moreover, it is extremely hygroscopic. It is a polymer compound containing hydrophilic and hydrophobic groups. It is slowly soluble in water and form a highly viscous transparent liquid whose 0.5% solution having a viscosity of about 1000cp with the viscosity being not as swelling as CMC and sodium alginate. But owing to the ion phenomenon of many anionic groups in the molecule makes the molecular chain being longer, increasing the apparent viscosity to form highly viscous solution. It has a viscosity which is 15-20 times as high as sodium carboxymethyl cellulose (CMC) and sodium alginate. It has a high alkali resistance with viscosity changing only little and it is also non-perishable. Heat treatment, neutral salts, and organic acids have very small effects on its viscosity. However, it has increased viscosity upon alkaline condition. Intense heating to 300 degrees will not cause decomposition of it. Due to its property as a kind of electrolyte, it is vulnerable to acids and metal ions which cause the decrease of viscosity. In case of more than a sufficient amount of divalent metal ions (e.g. aluminum, lead, iron, calcium, magnesium, zinc), it will form insoluble salt which cause intermolecular crosslink and thus gelation and further precipitation. But it is still as solution upon a low amount of divalent metal ion, making it be able to be used as detergent additives which play a role in preventing soil re-deposition.
Food grade sodium polyacrylate
In abroad, it has begun to apply sodium polyacrylate(9003-04-7) for being used in a variety of food for thickening, gluten and preservation since 1960s. In 2000, the Ministry of Health of china also officially approved it as a food grade thickener.
Application limitation: According to China's food additive standards.
The applications of food grade sodium polyacrylate used are as follows:
1. being used as a thickener in foods has the following effects:
(1) Enhance the adhesion ability to raw flour protein.
(2) Make starch particle to combine with each other and dispersion penetrate into the mesh structure of the protein.
(3) Form dough with a dense texture and being smooth in its glossy surface.
(4) It forms a stable dough colloid for preventing soluble starch exudation.
(5) It has a strong water-holding capacity which can make moisture be uniformly maintained in dough and prevent drying.
(6) It can be used to improve the dough extensibility.
(7) Make the raw material in the oil component be stably dispersed into the dough.
2. it is used as the electrolyte for protein interactions, change the protein structure, and enhance food viscoelasticity and improve the organization.
3. Application examples:
(1) Bread, cakes, noodles, macaroni, improve utilization of raw materials, improve the taste and flavor with the amount of 0.05%.
(2) Fish paste-like products, canned food, dried seaweed, etc., to strengthen its organization, to keep fresh flavor, enhanced sense of smell.
(3) Sauce, tomato sauce, mayonnaise, jam, cream, soy sauce, thickeners and stabilizers.
(4) Fruit juice, wine, etc., dispersants.
(5) Ice cream, Kara honey Seoul sugar, improve taste and the stability.
(6) Frozen food, aquatic products, surface jellies (preservation).
4. Owing to its slow dissolution rate in water; it can be pre-mixed with sugar, powdered starch syrup, emulsifier, etc., to improve the dissolution rate.
5. Sodium polyacrylate can be used as sugar, salt, beverage clarifying agent (polymer coagulant).
The above information is edited by the Chemicalbook of Dai Xiongfeng.
LD50> 10g/kg (mice by mouth).
Subacute test: rat 0.5g/kg/day or less, and for 6 months without exception.
GB 2760-2000: various types of food, 2.0 g/kg. The maximum amount was defined by 0.2% in Japan (1993).
White powder, odorless. Water-swellable, soluble in aqueous caustic soda.
1. It can be used as a corrosion scale inhibitor, water stabilizer, paint thickener and water retention agent, flocculants, drilling mud treatment agent.
2. The agent is used for the circulating cooling water treatment for equipment copper material with a excellent scale effect. At the amount of 100 mg/L, it can form chelate with the scale-forming ions in water of medium hardness and further flow with water, and can prevent the formation of iron oxide scale.
3. It can be used as a thickener and stabilizer in butter products, cream, tomato sauce. It can also be used as a dispersing agent in fruit juice, wine and spirits. It can improve the sense of taste of ice cream, and enhance its stability. It can also be used as surface freezing glue for freezing products and aquatic products, and can also play a role in preservation. It can also alter protein structure and enhance the viscoelasticity of food, and thus further improving the organization.
4. Thickener.
It has many functions in food as following: (1) Enhance the adhesion ability to raw flour protein. (2) Make starch particle to combine with each other and dispersion penetrate into the mesh structure of the protein. (3) Form dough with a dense texture and being smooth in its glossy surface. (4) It forms a stable dough colloid for preventing soluble starch exudation. (5) It has a strong water-holding capacity which can make moisture be uniformly maintained in dough and prevent drying. (6) It can be used to improve the dough extensibility. (7) Make the raw material in the oil component be stably dispersed into the dough. 2, it is used as the electrolyte for protein interactions, change the protein structure, and enhance food viscoelasticity and improve the organization. Application Example: (1) Bread, cakes, noodles, macaroni, improve utilization of raw materials, improve the taste and flavor with the amount of 0.05%. (2) Fish paste-like products, canned food, dried seaweed, etc., to strengthen its organization, to keep fresh flavor, enhanced sense of smell. (3) Sauce, tomato sauce, mayonnaise, jam, cream, soy sauce, thickeners and stabilizers. (4) Fruit juice, wine, etc., dispersants. (5) Ice cream, Kara honey Seoul sugar, improve taste and the stability. (6) Frozen food, aquatic products, surface jellies (preservation). 4, Owing to its slow dissolution rate in water; it can be pre-mixed with sugar, powdered starch syrup, emulsifier, etc., to improve the dissolution rate. 5, Sodium polyacrylate can be used as sugar, salt, beverage clarifying agent (polymer coagulant).
5. It can be used as a filtrate reducer in solid drilling industry.
6. This product is a good anion detergent and dispersants which can be combined with other water treatment agent compound used for oil field water, cooling water, boiler water treatment at high pH and at high concentration process without scaling.
1. Add deionized water and 34 kg of isopropanol chain transfer agent to the kettle separately and heat it to 80~82 °C. Add drop wise 14 kg of ammonium per-sulfate aqueous solution and 170 kg of acrylic monomers. After completion of dropping, perform the reaction for 3 h; cool to 40 °C; add 30% aqueous NaOH solution to a pH value of 8.0 to 9.0 and then have water and isopropanol been distilled to get the final liquid products. Spray dry to give a solid product.
2. Acrylate or acrylic acid is reacted with sodium hydroxide to get sodium acrylate, remove the alcohol by-produced; concentrate; adjust the pH, and undergo polymerization reaction to get the final product with the catalysis of ammonium per-sulfate.
3. Acrylic acid and sodium hydroxide is reacted to get sodium acrylate monomer, and then polymerize into sodium polyacrylate with ammonium per-sulfate as the catalyst.
4. Add sodium polyacrylate (with molecule weight: 1000~3000) to the reaction vessel to obtain 30% aqueous solution.
https://en.wikipedia.org/wiki/Sodium_polyacrylate
http://www.livestrong.com/article/458401-what-is-sodium-polyacrylate-how-is-it-used/
Sodium polyacrylate, also known as waterlock, is a sodium salt of poly acrylic acid with the chemical formula [-CH2-CH(COONa)-]n and broad application in consumer products. It has the ability to absorb as much as 200 to 300 times its mass in water. Sodium polyacrylate is anionic polyelectrolytes with negatively charged carboxylic groups in the main chain. While sodium neutralized poly acrylic acids are the most common form used in industry, there are also other salts available including potassium, lithium and ammonium.
faintly grey crystalline solid
Absorbent for aqueous-based spills. Retention and slow release aid for water.
sodium polyacrylate is a suspending agent, stabilizer, and emulsifier.
Scale inhibitor, builder in detergents, aid in soap and detergent processing and control of water hardness.
Sodium poly acrylate and other derivatives of polyacrylic acid have a wide variety of commercial and industrial uses that include:
Sequestering agents in detergents. ( By binding hard water elements such as calcium and magnesium, the surfactants in detergents work more efficiently.).
ChEBI: An organic sodium salt which is a macromolecule composed of repeating sodium acrylate units.
Poly(acrylic acid sodium salt) is a hydrophilic polymer, which can find wide applications in the production of consumer productslike diapers, because of its ability to absorb many more times its mass in water.
An eye irritant. When heated to decomposition it emits toxic fumes of Na2O.
Commercial polyacrylamide is first neutralised with an aqueous solution of NaOH, and the polymer is precipitated with acetone. The precipitate is redissolved in a small amount of water and freeze-dried. The polymer is then repeatedly washed with EtOH and water to remove traces of low-molecular-weight material, and finally dried in vacuum at 60o [Vink J Chem Soc, Faraday Trans 1 75 1207 1979]. It has also been dialysed overnight against distilled water, then freeze-dried. Sodium poly( -L-glutamate). Wash it with acetone, dry it in a vacuum, dissolve it in water and precipitate it with isopropanol at 5o. Impurities and low-molecular-weight fractions are removed by dialysis of the aqueous solution for 50hours, followed by ultrafiltration