Silicon

Gay Lussac and Thenard in 1809 obtained very impure amorphous silicon by passing silicon tetrafluoride over heated potassium. Berzelius in 1823 prepared elemental silicon in high purity by the same method. He also obtained silicon by heating potassium fluosilicate with potassium metal. Deville produced crystalline silicon in 1854 by electrolysis of a molten mixture of impure sodium aluminum chloride containing 10% silicon and a small quantity of aluminum.
Silicon is the second most abundant element on earth after oxygen. It occurs in nature combined with oxygen in various forms of silica and silicates. Silicates have complex structures consisting of SiO4 tetrahedral structural units incorporated to a number of metals. About 90% of the earth’s crust is made up of silica and naturally-occurring silicates. Silicon is never found in nature in free elemental form. Among all elements silicon forms the third largest number of compounds after hydrogen and carbon. There are well over 1,000 natural silicates including clay, mica, feldspar, granite, asbestos, and hornblende. Such natural silicates have structural units containing orthosilicates, SiO44– , pyrosilicates Si2O76– and other complex structural units, such as, (SiO3)n2n– that have hexagonal rings arranged in chains or pyroxenes (SiO32– )n and amphiboles, (Si4O116– )n in infinite chains. Such natural silicates include common minerals such as tremolite, Ca2Mg5(OH)2Si8O22; diopside, CaMg(SiO3)2; kaolin, H8Al4Si4O18; montmorillonite, H2Al2Si4O12; talc, Mg3[(OH)2 SiO10]; muscovite ( a colorless form of mica), H2KAl3(SiO4)3; hemimorphite, Zn4(OH)2Si2O7•H2O; beryl, Be3Al2Si6O18; zircon, ZrSiO4; benitoite, BaTiSi3O9; feldspars, KAlSi3O8; zeolites, Na2O•2Al2O3•5SiO2•5H2O; nephrite, Ca(Mg,Fe)3(SiO3)4; enstatite, (MgSiO3)n; serpentine, H4Mg3Si2O9; jadeite, NaAl(SiO3)2; topaz, Al2SiO4F2; and tourmaline, (H,Li,K,Na)9 Al3(BOH)2Si4O19. Many precious gemstones are silicate based. Such gems include beryl, emerald, aquamarine, morganite, topaz, tourmaline, zircon, amazon stone and moonstone.

Elemental silicon has some of the most important applications in this electronic age. One of the major applications is in computer chips. The single crystals of crystalline silicon are used for solid-state or semiconductor devices. Silicon of hyperpurity, doped with trace elements, such as boron, phosphorus, arsenic, and gallium is one of the best semiconductors. They are used in transistors, power rectifiers, diodes and solar cells. Silicon rectifiers are most efficient in converting a-c to d-c electricity. Hydrogenated amorphous silicon converts solar energy into electricity.

​The space lattice of Si belongs to the cubic system, and its diamond structure has a lattice constant of a=0.543072 nm (258℃) and Si–Si=0.235 nm.

Elemental silicon is produced commercially by heating silica with carbon (coke) in an electric furnace using carbon electrodes:
SILICON 819SiO2 + C → Si + CO2
The product obtained is about 96 to 98% purity. Repeated leaching forms about 99.7% purified product. Alternatively, lower grade silicon is converted to its halide or halosilane, which is then reduced with a high purity reducing agent. Hyperpure silicon for semiconductor applications can be made by several methods. Such processes include reduction of silicon tetrachloride with highly pure zinc:
SiCl4 + 2Zn → Si + 2ZnCl2
or by reducing trichlorosilane with hydrogen at 1,150°C using a silicon filament on which deposition of silicon occurs:
SiHCl3 + H2 → Si + 3HCl
or by heating silane or silicon tetraiodide to elevated temperatures:
SiH4 → Si + 2H2
SiI4 → Si + 2I2
or by reducing silicon tetrafluoride with sodium:
SiF4 + 4Na → Si + 4 NaF
Several processes are known to achieve growth of single crystals of silicon for semiconductors. One such method developed in 1918 is known as Czocharlski process or Teal-Little method. The process involves dipping a single crystal “seed” into molten silicon held at the melting point. The seed is properly oriented by rotation and the molten silicon is allowed to freeze gradually over it and the seed is slowly withdrawn. The growth rate is controlled by melt temperature and heat losses from the crystal. Growth rates are usually in the range of 2.5 cm/hour but can vary with diameter. Crystals of varying sizes have been produced by this method. The common sizes of crystals usually range between 75 to 125 mm in diameter and about 100 cm long. Pure quartz crucibles or silicon pedestals are employed to carry out single crystal’s growth.

grey lustrous solid or grey powder

Silicon is a nonmetallic element which is known as silicon metal. Not occur freely in nature, but is found in silicon dioxide (silica) and in various silicates. It is a steel-gray crystalline solid or a black-brown amorphous material.

Silicon does not occur free in nature, but is found in most rocks, sand, and clay. Siliconis electropositive, so it acts like a metalloid or semiconductor. In some ways silicon resemblesmetals as well as nonmetals. In some special compounds called polymers, silicon will act inconjunction with oxygen. In these special cases it is acting like a nonmetal.
There are two allotropes of silicon. One is a powdery brown amorphous substance bestknown as sand (silicon dioxide). The other allotrope is crystalline with a metallic grayishluster best known as a semiconductor in the electronics industry. Individual crystals of siliconare grown through a method known as the Czochralski process. The crystallized siliconis enhanced by “doping” the crystals (adding some impurities) with other elements such asboron, gallium, germanium, phosphorus, or arsenic, making them particularly useful in themanufacture of solid-state microchips in electronic devices.
The melting point of silicon is 1,420°C, its boiling point is 3,265°C, and its density is2.33 g/cm³.

There are 21 isotopes of silicon, three of which are stable. The isotope Si-28makes up 92.23% of the element’s natural abundance in the Earth’s crust, Si-29 constitutes4.683% of all silicon found in nature, and the natural abundance of Si-30 ismerely 3.087% of the stable silicon isotopes found in the Earth’s crust.

Silicon was named after the Latin word silex, which means “flint.”

Silicon, in the form of silicon dioxide (SiO₂), is the most abundant compound in theEarth’s crust. As an element, silicon is second to oxygen in its concentration on Earth, yet it is only the seventh most abundant in the entire universe. Even so, silicon is used as the standard(Si = 1) to estimate the abundances of all other elements in the universe. For example, hydrogenequals 40,000 times the amount of silicon in the cosmos. Hydrogen is the most abundantof all elements in the universe, and carbon is just three and half times as abundant as siliconin the entire universe. On Earth silicon accounts for 28% of the crust, oxygen makes up 47%of the crust, and much of the rest of the crust is composed of aluminum.
It is believed that silicon is the product of the cosmic nuclear reaction in which alpha particleswere absorbed at a temperature of 10⁹ Kelvin into the nuclei of carbon-12, oxygen-16,and neon-20. Pure elemental silicon is much too reactive to be found free in nature, but it doesform many compounds on Earth, mainly oxides as crystals (quartz, cristobalite, and tridymite)and amorphous minerals (agate, opal, and chalcedony). Elemental silicon is produced byreducing silica (SiO₂) in a high-temperature electric furnace, using coke as the reducing agent.It is then refined. Silicon crystals used in electronic devices are “grown” by removing startercrystals from a batch of melted silicon.

The characteristics of silicon in some ways resemble those of the element germanium,which is located just below it in the carbon group.
Flint is the noncrystalline form of silicon and has been known to humans since prehistorictimes. When struck with a sharp blow, flint would flake off sharp-edged chips that were thenused as cutting tools and weapons.
In addition to silica (silicon dioxide SiO₂), the crystal form of silicon is found in severalsemiprecious gemstones, including amethyst, opal, agate, and jasper, as well as quartz of varyingcolors. A characteristic of quartz is its piezoelectric effect. This effect occurs when thequartz crystal is compressed, producing a weak electrical charge. Just the opposite occurs whenelectric vibrations are fed to the crystal. These vibrations are then duplicated in the crystal.Quartz crystals are excellent timekeeping devices because of this particular characteristic.

Davy in 1800 thought silica to be a compound and not an element; later in 1811, Gay Lussac and Thenard probably prepared impure amorphous silicon by heating potassium with silicon tetrafluoride. Berzelius, generally credited with the discovery, in 1824 succeeded in preparing amorphous silicon by the same general method as used earlier, but he purified the product by removing the fluosilicates by repeated washings. Deville in 1854 first prepared crystalline silicon, the second allotropic form of the element. Silicon is present in the sun and stars and is a principal component of a class of meteorites known as “aerolites.” It is also a component of tektites, a natural glass of uncertain origin. Natural silicon contains three isotopes. Twenty-four other radioactive isotopes are recognized. Silicon makes up 25.7% of the Earth’s crust, by weight, and is the second most abundant element, being exceeded only by oxygen. Silicon is not found free in nature, but occurs chiefly as the oxide and as silicates. Sand, quartz, rock crystal, amethyst, agate, flint, jasper, and opal are some of the forms in which the oxide appears. Granite, hornblende, asbestos, feldspar, clay mica, etc. are but a few of the numerous silicate minerals. Silicon is prepared commercially by heating silica and carbon in an electric furnace, using carbon electrodes. Several other methods can be used for preparing the element. Amorphous silicon can be prepared as a brown powder, which can be easily melted or vaporized. Crystalline silicon has a metallic luster and grayish color. The Czochralski process is commonly used to produce single crystals of silicon used for solid-state or semiconductor devices. Hyperpure silicon can be prepared by the thermal decomposition of ultra-pure trichlorosilane in a hydrogen atmosphere, and by a vacuum float zone process. This product can be doped with boron, gallium, phosphorus, or arsenic to produce silicon for use in transistors, solar cells, rectifiers, and other solid-state devices that are used extensively in the electronics and space-age industries. Hydrogenated amorphous silicon has shown promise in producing economical cells for converting solar energy into electricity. Silicon is a relatively inert element, but it is attacked by halogens and dilute alkali. Most acids, except hydrofluoric, do not affect it. Silicones are important products of silicon. They may be prepared by hydrolyzing a silicon organic chloride, such as dimethyl silicon chloride. Hydrolysis and condensation of various substituted chlorosilanes can be used to produce a very great number of polymeric products, or silicones, ranging from liquids to hard, glasslike solids with many useful properties. Elemental silicon transmits more than 95% of all wavelengths of infrared, from 1.3 to 6.7 μm. Silicon is one of man’s most useful elements. In the form of sand and clay it is used to make concrete and brick; it is a useful refractory material for high-temperature work, and in the form of silicates it is used in making enamels, pottery, etc. Silica, as sand, is a principal ingredient of glass, one of the most inexpensive of materials with excellent mechanical, optical, thermal, and electrical properties. Glass can be made in a very great variety of shapes, and is used as containers, window glass, insulators, and thousands of other uses. Silicon tetrachloride can be used to iridize glass. Silicon is important in plant and animal life. Diatoms in both fresh and salt water extract silica from the water to build up their cell walls. Silica is present in ashes of plants and in the human skeleton. Silicon is an important ingredient in steel; silicon carbide is one of the most important abrasives and has been used in lasers to produce coherent light of 4560 ?. A remarkable material, first discovered in 1930, is Aerogel, which is now used by NASA in their space missions to collect cometary and interplanet dust. Aerogel is a highly insulative material that has the lowest density of any known solid. One form of Aerogel is 99.9% air and 0.1% SiO2 by volume. It is 1000 times less dense than glass. It has been called “blue smoke” or “solid smoke.” A block of Aerogel as large as a person may weigh less than a pound and yet support the weight of 1000 lbs (455 kg). This material is expected to trap cometary particles traveling at speeds of 32 km/sec. Aerogel is said to be non-toxic and non-inflammable. It has high thermal insulating qualities that could be used in home insulation. Its light weight may have aircraft applications. Regular grade silicon (99.5%) costs about $160/kg. Silicon (99.9999%) pure costs about $200/kg; hyperpure silicon is available at a higher cost. Miners, stonecutters, and other engaged in work where siliceous dust is breathed in large quantities often develop a serious lung disease known as silicosis.

Silicon’s tetravalent pyramid crystalline structure, similar to tetravalent carbon, results ina great variety of compounds with many practical uses. Crystals of silicon that have beencontaminated with impurities (arsenic or boron) are used as semiconductors in the computerand electronics industries. Silicon semiconductors made possible the invention of transistorsat the Bell Labs in 1947. Transistors use layers of crystals that regulate the flow of electric current.Over the past half-century, transistors have replaced the vacuum tubes in radios, TVs,and other electronic equipment that reduces both the devices’ size and the heat produced bythe electronic devices.
Silicon can be used to make solar cells to provide electricity for light-activated calculatorsand satellites. It also has the ability to convert sunlight into electricity.When mixed with sodium carbonate (soda ash) and calcium carbonate (powdered limestone)and heated until the mixture melts, silica (sand) forms glass when cooled. Glass ofall types has near limitless uses. One example is Pyrex, which is a special heat-resistant glassthat is manufactured by adding boron oxide to the standard mixture of silica, soda ash, andlimestone. Special glass used to make eyewear adds potassium oxide to the above standardmixture.
Silicon is also useful as an alloy when mixed with iron, steel, copper, aluminum, andbronze. When combined with steel, it makes excellent springs for all types of uses, includingautomobiles.
When silicon is mixed with some organic compounds, long molecular chains known assilicone polymers are formed. By altering the types of organic substances to these long siliconepolymer molecules, a great variety of substances can be manufactured with varied physicalproperties. Silicones are produced in liquid, semisolid, and solid forms. Silicones may berubbery, elastic, slippery, soft, hard, or gel-like. Silicone in its various forms has many commercialand industrial uses. Some examples are surgical/reconstructive implants, toys, SillyPutty, lubricants, coatings, water repellents for clothing, adhesives, cosmetics, waxes, sealants,and electrical insulation.

silicone (volatile) is used in face creams to increase the product’s protection capabilities against water evaporation from the skin. Silicone polyethers are mainly used in water-based skin care formulations and give improved softness, gloss, and feel. Silicones have been used in cosmetics for more than 30 years. They are minerals able to repel water. Silicones present formulation problems because of poor compatibility with cosmetic oils and emollients. Silicones are not irritating.

Silicon is usually available as electronic-grade, high-quality, high-purity single crystalline material in the form of wafers (round, surface-polished slices typically of 4–12 inches in diameter and a few hundreds of micrometers to millimeters in thickness). The biggest advantage of using silicon for microfluidic applications is the availability of a mature processing technology inherited from the microelectronics IC industry as well as the possibility of defining very small structures that can be cointegrated with the electronics on the same chip. Some of the disadvantages of using silicon as a structural material are linked to the polar nature of the silicon crystal resulting in undesirable adsorption of molecules in microfluidic systems. Furthermore, the higher cost of silicon as substrate material without any specific advantages from microfluidic systems standpoint makes it less attractive as a substrate material unless integration of on-chip electronic circuits is a strong requirement for the particular microsystem design. The typical cost of an average quality silicon substrate is about 0.25 U.S. cents/cm2.

In making silanes and silicones, the Si-C bond being about as strong as a C-C bond. In the manufacture of transistors, silicon diodes and similar semiconductors. For making alloys such as ferrosilicon, silicon bronze, silicon copper. As a reducing agent like aluminum in high tempereture reactions.

silicon: Symbol Si. A metalloid element belonging to group 14 (formerlyIVB) of the periodic table; a.n.14; r.a.m. 28.086; r.d. 2.33; m.p.1410°C; b.p. 2355°C. Silicon is thesecond most abundant element inthe earth’s crust (25.7% by weight) occurring in various forms of silicon(IV)oxide (e.g. quartz) and in silicateminerals. The element is extractedby reducing the oxide with carbon inan electric furnace and is used extensivelyfor its semiconductor properties.It has a diamond-like crystalstructure; an amorphous form alsoexists. Chemically, silicon is less reactivethan carbon. The element combineswith oxygen at red heat and isalso dissolved by molten alkali. Thereis a large number of organosiliconcompounds (e.g. siloxanes) althoughsilicon does not form the range ofsilicon–hydrogen compounds andderivatives that carbon does (seesilane). The element was identifiedby Antoine Lavoisier in 1787 andfirst isolated in 1823 by J?ns Berzelius.

Nonmetallic element Atomic number 14, group IVA of the periodic table, aw 28.086, valence = 4, three stable isotopes. It is the second most abundant ele- ment (25% of the earth’s crust) and is the most important semiconducting element; it can form more co

Si is a little soluble in water (Solubility: 0.005 g/100 g H2O (298 K)). It reacts strongly with F at room temperature, Cl at 430℃, Br at 500℃, O at 400℃, and N2 at 1000℃ to form compounds of SiF4 , SiCl4 , SiBr4 , SiO2 , SiO, and Si3N4 , respectively.

A dark brown powder. Insoluble in water and denser than water. Burns readily when exposed to heat or flames, and may be difficult to extinguish. Water may not be effective in extinguishing flames. Used to make computer microchips.

Highly flammable. Insoluble in water. A significant dust explosion hazard.

Silicon is a reducing agent. Ignites in fluorine gas at ordinary temperatures [Mellor 2:11-13 1946-47]. Burns spontaneously in gaseous chlorine. A mixture of silicon, aluminum, and lead oxide explodes when heated [Mellor 7:657 1946-47]. When heated with an alkali carbonate, a vigorous reaction attended by incandescence occurs [Mellor 6:164 1946-47]. Reacts violently with silver fluoride [Mellor 3:389 1946-47]. Reacts with sodium-potassium alloy to form sodium silicide, which is spontaneously flammable in air [Mellor 2 Supp. 2:564 1961].

Flammable in powder form.

The dust of silicon oxide (silicate) can burn or explode and is very harmful if inhaled.Continued exposure to silica dust causes silicosis, a form of pneumonia.
The hydrides of silicon (silicon plus hydrogen) are extremely volatile and spontaneouslyburst into flames in air at room temperatures. They must be kept in special vacuum chambers.
Over the past several decades, there has been some concern over the potential hazards andsafety of the cosmetic use of silicone body implants—breast implants, in particular. Severalmanufactures have been sued over the failure of the implants, and the federal government (FDA) withdrew its approval for their use. Congressional hearings with manufacturers in2005 produced new information that has reversed the FDA’s ban on their use—but only withcertain manufacturers of implants. The debate continues.

Oxides from metallic fires are a severe health hazard. Inhalation or contact with substance or decomposition products may cause severe injury or death. Fire may produce irritating, corrosive and/or toxic gases. Runoff from fire control or dilution water may cause pollution.

May react violently or explosively on contact with water. Some are transported in flammable liquids. May be ignited by friction, heat, sparks or flames. Some of these materials will burn with intense heat. Dusts or fumes may form explosive mixtures in air. Containers may explode when heated. May re-ignite after fire is extinguished.

Non flammable

Some plants need silicon (Si) in addition to micro and macro nutrients. It is one of the most abundant elements absorbed by plants. Silicon belongs to Group 14 (formerly IVB) of the Periodic Table. It is an essential trace element for the normal growth of higher animals, as it is involved in the formation of bones and cartilages. Crops grown in the absence of soluble silica are more prone to mildews than those provided with soluble silica. Rice, cucumber, gherkin and barley require silicon. Silicon improves the growth of sugar cane. Silicon corrects soil toxicities arising from the presence of excessive quantities of Mn, Fe and active Al. The oxidizing power of rice roots and their tolerance to the high level of iron and manganese are attributed to silicon nutrition.
In a field trial, when parts of a rice crop had a silica to nitrogen ratio of 11:2, 10 tons/ha of extra rice was produced. Silicon helps to (a) maintain the erectness of rice leaves, (b) increase resistance to insect pests, (c) improve photosynthesis, (d) increase the number of stems, and (e) improve the fresh as well as dry weights of rice plants. If silica is withheld during the reproductive period, the number of spikelets per panicle and the ripened grain percentage decreases.
Silicon contributes to the structure of cell wall, thus (a) making the cell wall more immune to diseases, (b) improving the stalk strength, and (c) increasing the resistance to lodging. Rice and sugar cane respond favorably to silicon fertilizers. Enzyme-silicon complexes formed in sugar cane act as protectors or regulators of photosynthesis and enzyme activity. By suppressing the invertase activity in sugar cane, silicon increases sugar production.
Silicon and oxygen occupy 75% of the earth's crust, of which silicon alone is 27.7%. Silica, which occurs to the extent of 60 to 80% as insoluble quartz silica, is in the form of mono-silicic acid [Si(OH)₄], the availability of which increases with increasing soil pH and temperature. Roughly, 130 ppm silicon (SO₂) is the critical limit of the available silicon in air-dry soil for maximizing wetland rice yield; the critical limit is raised by adding silicon (as SiO₂).
Silicon uptake by plants differ with plant species. Gramineae contains 10 to 20 times more silicon than that normally found in legumes and dicotyledons. Paddy contains 4.6 to 7.0% of silicon in the straw. Oxides of iron and aluminum, liming, flooding and nutrient supply influence silicon-uptake; high soil-water content increases the uptake in rice, barley, oats, sorghum and sugar cane.
The quantity of silica fertilizer to be added to the soil is guided by the ratio of the available silica to organic matter, which if less than 100, warrants the use of fertilizer; if the ratio is more than 100, it calls for the addition of organic matter; if less than 50, it indicates that the soil is suffering from silicon shortage. For a silicondeficient area, the addition of 2 todha of silica fertilizer is recommended. Freckling, which is a necrotic leaf spot condition, is a symptom of low levels of silicon in a sugar cane plant that receives direct sunlight, the ultraviolet (W) radiation in sunlight being the causative agent. Sufficient quantities of silicon in a sugar cane plant filters out harmful UV radiation.
Major silica fertilizers include calcium silicate slag, calcium silicate and sodium meta-silicate. 1.5 to 2.0 tons of silicate slag per hectare usually provides sufficient silicon for rice crops produced in low-silicon soils. Silicate fertilizers serve as a source of silicon and a liming material in acid soils. Slags from the steel industry, ground basic-slag (containing varying quantities of Al, Ca, Fe, Mn, Mg and Si), and wollastonite (Ca-Mg silicate) are all silicate fertilizers.
Sodium silicate increases the crop yield in phosphatedeficient soils, possibly because silicates help increase the assimilation of phosphoric acid by the plant and not the soil. However, according to some, silicate increases the amount of available soil phosphate. Heavy applications of nitrogen make the rice plant more susceptible to fungal attack because of the decreased silicon concentration in the straw.

Silicon is, after oxygen, the second most abundant element in the earth s crust. It occurs in a range of minerals and sand (SiO2, quartz). Silicon can be extracted from silicates or sand by reducing SiO2 with coke at high temperatures at around 3000°C.Silicon is used in a wide variety of applications. In nature, silicon does not exist as the pure metal and most commonly occurs in silica (including sand) and silicates. Silicon dioxide, also known as silica, is a hard substance with a high melting temperature and clearly very different from carbon dioxide. Molten silica can be used to make glass, an extremely useful material, which is resistant to attack by most chemicals except fluorine, hydrofluoric acid and strong alkalis. Silicon atoms can also be found in the class of compounds called silicones. Pure silicon metal is used in semiconductors, the basis of all electronic devices, and is most well known for its application in solar panels and computer chips.

A nuisance dust. Moderately toxic by ingestion. An eye irritant. Does not occur freely in nature, but is found as sdicon dioxide (sdtca) and as various shcates. Elemental Si is flammable when exposed to flame or by chemical reaction with oxidlzers. Violent reactions with alkali carbonates, oxidants, (A1 + PbO), Ca, Cs2C2, Cl2, CoF2, F2, IFs, MnF3, Rb2C2, FNO, AgF, NaK alloy. When heated it will react with water or steam to produce H2; can react with oxidizing materials. See also various silica entries, SILICATES, and POWDERED METALS.

Silicon may be used in the manufacture of silanes, silicon tetrachloride, ferrosilicon, silicones. It is used in purified elemental form in transistors and photovoltaic cells.

UN1346 Silicon powder, amorphous requires, Hazard Class: 4.1; Labels: 4.1-Flammable solid.

Dust or powder may form explosive mixture with air. A strong reducing agent. Incompatible with oxidizers (chlorates, nitrates, peroxides, permanganates, perchlorates, chlorine, bromine, fluorine, etc.); contact may cause fires or explosions. Keep away from alkaline materials, strong bases, strong acids, oxoacids, epoxides, calcium, carbonates, chlorine, fluorine, oxidizers, cesium carbide; alkaline carbonates.