  Poly(vinyl formal) is generally prepared directly from poly(vinyl acetate) without isolation ofthe intermediate poly(vinyl alcohol). In a typical process, poly(vinyl acetate) is dissolved in acetic acid and then formalin and a small quantity of sulphuric acid (catalyst) are added. The mixture is heated at 70°C for 24 hours. Water is then added to the product with rapid agitation and the poly(vinyl formal) is precipitated as granules, which are washed with alkali and dried.
  As the formal content increases there is a progressive increase in softening point, impact strength and hardness. The materials, being amorphous, are soluble in solvents of similar solubility parameter, such as dichloroethylene and dioxan; as the acetate content increases, the polymers become more soluble in ketones, esters and glycol ethers.
  The principal use of poly(vinyl formal) is in the electrical insulation of magnet wire. For this purpose, polymers with low hydroxyl content (5-6%) and low acetate content (10-13%) are used in admixture with a resol phenolic resin. On heating at about 175°C, cross-linking occurs; this reaction probably involves the formation of ether links by condensation of methylol groups in the resol and hydroxyl groups in the poly(vinyl formal). These coatings are extremely tough; of particular significance is the fact that they are able to withstand high-speed winding operations.

ポリビニルホルマール 生産企業

Global(2)Suppliers

26876-25-5, ポリビニルホルマール キーワード